Product description: Products Detail Caustic Calcined Magnesite : Mainly used in improving field, feed additives,magnesium oxychloride cement,etc. MgO: ≥95%;LOI:≤4% ; SiO2: ≤2% ; CaO:≤2% MgO: ≥92%;LOI:≤5% ; SiO2: ≤3% ; CaO:≤2% MgO: ≥90%;LOI:≤6% ; SiO2: ≤4% ; CaO:≤2% MgO: ≥87%;LOI:≤7% ; SiO2: ≤5% ; CaO:≤3% MgO: ≥85%;LOI:≤8% ; SiO2: ≤6% ; CaO:≤3% MgO: ≥80%;LOI:≤10% ; SiO2: ≤8% ; CaO:≤5% MgO: ≥70%;LOI:≤12% ; SiO2: ≤10% ; CaO:≤5% Electrically Fused Magnesite : Mainly used in producing magnesite carbon brick,aluminium magnesite carbon brick,insulation Material ,refractories etc. MgO>98 , SiO2<0.35% , CaO<0.7%,B.D(g/cm3)>3.5 IL<0.2% MgO>97 , SiO2<0.6% , CaO<1.2%,B.D(g/cm3)>3.5 IL<0.2% MgO>96 , SiO2<0.8% , CaO<1.6%,B.D(g/cm3)>3.45IL<0.2% MgO>97.5 , SiO2<0.7% , CaO<1.5%,B.D(g/cm3)>3.5IL<0.2% MgO>96.5 , SiO2<0.8% , CaO<1.4%,B.D(g/cm3)>3.5IL<0.2% MgO>95.5, SiO2<1.0% , CaO<2.0%,B.D(g/cm3)>3.45IL<0.2% dead burnt magnesite: MgO>97.2 SiO2<0.5 , CaO<1.15,B.D(g/cm3)>3.30 IL<0.3% MgO>97.2 SiO2<0.6 , CaO<1.2,B.D(g/cm3)>3.30 IL<0.3% MgO>97 , SiO2<0.7 , CaO<1.2,B.D(g/cm3)>3.30 IL<0.3% MgO>97 , SiO2<0.8, CaO<1.2%,B.D(g/cm3)>3.30IL<0.3% MgO>96 , SiO2<1.2 , CaO<1.6,B.D(g/cm3)>3.25IL<0.3% MgO>93 , SiO2<3.5 , CaO<1.6,B.D(g/cm3)>3.18IL<0.3% MgO>92 , SiO2<4.0 , CaO<1.6,B.D(g/cm3)>3.18 IL<0.3% MgO>91 , SiO2<4.5, CaO<1.8,B.D(g/cm3)>3.20IL<0.3% MgO>90 , SiO2<4.5 , CaO<2.0,B.D(g/cm3)>3.18IL<0.3% MgO>89 , SiO2<5.0 , CaO<2.5,B.D(g/cm3)>3.15IL<0.3%