Home > Offer to Sell > Catalyst and Auxiliary > Plastic Auxiliary Agent > Halogen-free flame retardant specialized for modified PA66

Halogen-free flame retardant specialized for modified PA66

Inquiry
  Post Date: Jun 01,2016
  Expiry Date: Nov 28,2016
  Detailed Description: Cas No. :225789-38-8 Specs:LFR-8006
LFR-8006
Halogen-free flame retardant specialized for modified PA66

1. Introduction:
LFR-8006 is one P&N synergistic flame retardant. It is white powder with low dust, high temperature resistance and non-migration. It is mainly applied to engineering plastics such as nylon 6 and PA66 (glass fiber reinforced and unreinforced) series and TPE (TPEE, TPU and PEBA).

2. Specification:
Item Unit Target value
P content %(w/w) 19-20%
Density g/cm3 1.25
Bulk density g/cm3 0.30-0.40
Moisture %(w/w) <0.25
Initial decomposition temperature ℃ >350
Average particle size(D50) μm 30-40

3. Application:
a. 8006 is especially suitable for nylon system (PA6, PA66 etc) with high glass fiber reinforced. The flame retardant nylon can achieve excellent mechanical and electrical properties.
b. In glass fiber reinforced PA6 or PA66, the additive amount of LFR-8006 is 15-20wt%, which could enable the material to reach UL94 V0 rating at 0.8mm-1.6mm thickness. Subject to the polymer grade, processing condition and glass fiber reinforcement, the additive amount of this flame retardant may vary.
c. 8006 has better thermal stability, wide processing window to various equipment, and the flame retardant performance is efficient and very stable.
d. 8006 can also be compounded with other efficient halogen-free flame retardant (synergist) to further improve comprehensive mechanical and electric properties, which help to satisfy the increasing stringent demands of terminal applications of plastic modification industry.

Suggestion of usage
In the processing, it is important to pre-dry the polyamide before mixing with LFR-8006. If possible, the resulting moisture content should be below 0.1% (by wt.). Pre-drying of LFR-8006 is not necessary. However, pre-drying (at 120℃ for 4 hours) is recommended, if very low moisture contents must be avoided.
The mixing and processing methods customary in powder processing of polymers can be used with LFR-8006. Prevention of dust fires and dust explosions or the relevant national regulations must be observed.
The optimum conditions for incorporating should be determined in each individual case. Care must be taken to ensure homogeneous dispersion of all components. The temperature of the polymer melt should not exceed 320℃.

4. Packaging & Storage:
20KG in one paper-plastic composite bag, which is lined with plastic bag
Sealed storage in dry, dust-proof and cool place

  CAS Registry Number:

225789-38-8

  Synonyms: ;Aluminum tris(diethylphosphinate);Aluminum diethylphosphinate;Diethylphosphinic acid aluminum salt;Diethyl Phosphinic Acid Aluminum;Ammonium polyphosphate(APP-0MF*);Ammonium polyphosphate(APP-0M);
  Molecular Formula: C12H30AlO6P3
  Molecular Weight: 390.2658
  Molecular Structure: 225789-38-8 Diethylphosphinic Acid, Aluminum Salt

  Company: Jiangsu Liside New Material Co., Ltd.     [ China ]        
  Contact: Jason Huang
  Tel: +86-523-88660000
  Fax: +86-523-88663699
  Email: jason@liside.com
Disclaimer statement:The information and data included above have been realized by the enterprises and compiled by the staff, and are subject to change without notice to you. The Chemnet makes no warranties or representations whatsoever regarding the facticity, accuracy and validity of such information and data. In order to ensure your interest, we suggest you chose the products posted by our gold suppliers or VIP members.