Master Batch of Antimony Trioxide(FR-M1220)

Inquiry
  Post Date: Jun 07,2017
  Expiry Date: Dec 04,2017
  Detailed Description:
This master batch of Antimony Trioxide (Sb2O3)is designed to eliminate the pollution brought by powder. It can be compounded with polymers without modified particle-shaping and features in fine disperse properties. The anti-impact strength of polymers with this master batch is remarkably improved as compared to these of the powder Antimony Trioxide (Sb2O3), which make it applicable in such polymer as PA6, PA66, ABS, PP, PE, PBT, PVC, HIPS,, etc..
 
Technical Indexes:
Item
Index
Appearance
White Pellets
Particle Size
Φ3mm×2mm
 Sb2O3
90 %
Whiteness
≥95
Moisture
≤0.2%
PbO
≤0.06%
As
≤0.04%
Cu
≤0.0013%
Se
≤0.0008%
Fe
≤0.0014%
Cd
≤0.0008%
 
Applications:
FR-M1220 could be directly blent with resin and appropriate amount of master batch of decabromodiphenyl oxide (or other halogen flame retarding agent). The particle-shaping can be achieved by injection or twin-screw extrusion after mixed.
 
 Packing:25Kg or 1000Kg plastic woven bag
 
Recommended:
Resin
ABS
HIPS
PA
Master Batch
FR-M1210(%)
FR-M1220(%)
FR-M1210(%)
FR-M1220(%)
FR-M1210(%)
FR-M1220(%)
V-0
12
5
12
5
13.5
5.5
V-1
11.0
4.2
11.0
4.2
11.5
4.5
V-2
10
3.5
10
3.5
10.5
3.5
HB
2.5
1
2.5
0.8
4.5
1.5
 
Application:(ABS)
Property
Unit
Method
1
2
Simple Beam Notch Impact Strength
KJ/m2
GB/T 1043
8.0
8.9
Izod Impact Strength
KJ/m2
GB/T 1843
8.2
7.4
Average Shrinkage
%
HG-112
-0.70
-0.57
Tensile Strength
MPa
GB/T 1040
42.5
42
Elongation at Break
%
GB/T 1040
20
25
Simple Beam Impact Strength
KJ/m2
GB/T 1043
58.5
63.5
UL 94
-
ANSI/UL 94
V-0
V-0
LOI
%
ASTM-2863
26.5
29.8
Maximum Smoke Density
-
ASTM E-662
266.6
247.5
Thermal Distortion Temperature
℃
GB 1634
95.5
97
 
Formulation 1: ABS 82%;Saytex102E(powder) 12.5%;Sb2O3 (powder) 4.5%; other additive 1%
Formulation 2:  ABS 80%;FR-M1220 4.5% ; FR-M1210 14.5%;other additive 1%
 
Dose recommended:
Resin
ABS
HIPS
PA
Master Batch
FR-M8010 (%)
FR-M1220(%)
FR-M8010 (%)
FR-M1220(%)
FR-M8010 (%)
FR-M1220(%)
V-0
11.5
5
11.5
5
13.5
5
V-1
11.0
4.5
11.0
4.5
11.5
4.5
V-2
10.5
3.5
10.5
3.5
11
3.5
HB
2.5
1
2.5
0.8
5
1.5
 
Application Information:(ABS)
 
Property
Unit
Method
1
2
Simple Beam Notch Impact Strength
KJ/m2
GB/T 1043
8
11.5
Izod Impact Strength
KJ/m2
GB/T 1843
8.2
9.5
Average Shrinkage
%
HG-112
-0.72
-0.6
Tensile Strength
MPa
GB/T 1040
42.5
42.2
Elongation at Break
%
GB/T 1040
21
26.5
Simple Beam Impact Strength
KJ/m2
GB/T 1043
58.5
62.5
UL 94
-
ANSI/UL 94
V-0
V-0
LOI
%
ASTM-2863
26.5
28
Maximum Smoke Density
-
ASTM E-662
265
170
Thermal Distortion Temperature
℃
GB 1634
95
95
 
Formulation 1:ABS 82.3%;Saytex8010(powder) 12.5%;Sb2O3 (powder) 4.2%; other additive 1%
Formulation 2:  ABS 80%;FR-M1220 4.5% ;  FR-M8010  14.5%; other additive 1
 
Dose recommended:
 
ABS %
HIPS %
PA %
V-0
17
17
18
V-1
14
14
14
V-2
12.5
12.5
12.5
HB
3.5
3.5
6.5
 
Application Information:(ABS 757K)
Property
Unit
Method
1
2
Tensile Strength
MPa
GB/T 1040
42.5
41.5
Elongation at Break
%
GB/T 1040
20
25
Simple Beam Impact Strength
KJ/m2
GB/T 1043
58.5
63.5
Simple Beam Notch Impact Strength
KJ/m2
GB/T 1043
8
8.5
Izod Notch Impact Strength
KJ/m2
GB/T 1843
8.3
8.9
Average Dimension Change
%
HG-112
-0.71
-0.65
UL 94
-
ANSI/UL 94
V-0
V-0
LOI
%
ASTM-2863
26.5
29.5
Maximum Smoke Density
-
ASTM E-662
268.5
244.5
Thermal Distortion Temperature
℃
GB 1634
96
96
Formulation 1:ABS 83%;DBDPO 12%;Sb2O3 4%;other 1%
Formulation 2:ABS 83%;FR2000 17%
 
Dose recommended:
 
ABS %
HIPS %
PA %
V-0
16.7
16.7
18.2
V-1
14.2
14.2
14.2
V-2
12.5
12.5
12.5
HB
3.2
3.2
6.3
 
Application Information:(ABS 757K)
Property
Unit
Method
1
2
Tensile Strength
MPa
GB/T 1040
42.5
41.5
Elongation at Break
%
GB/T 1040
20
25
Simple Beam Impact Strength
KJ/m2
GB/T 1043
58.5
63.5
Simple Beam Notch Impact Strength
KJ/m2
GB/T 1043
8
8.5
Izod Notch Impact Strength
KJ/m2
GB/T 1843
8.2
9
Average Dimension Change
%
HG-112
-0.70
-0.65
UL 94
-
ANSI/UL 94
V-0
V-0
LOI
%
ASTM-2863
26.5
28
Maximum Smoke Density
-
ASTM E-662
265.5
169.5
Thermal Distortion Temperature
℃
GB 1634
96
94
 
Formulation 1:ABS 83%;DBDPE 125%;Sb2O3 4% ;other 1%
Formulation 2:ABS 83%;FR3000 17%


  Company: Weifang Yucheng Chemical Co.,Ltd.     [ China ]        
  Contact: MR.ALLAN WEI(MANAGER) 013906369909
  Tel: +86-536-8291528 8291538 013906
  Fax: +86-536-8291558
  Email: brom@163169.net
Disclaimer statement:The information and data included above have been realized by the enterprises and compiled by the staff, and are subject to change without notice to you. The Chemnet makes no warranties or representations whatsoever regarding the facticity, accuracy and validity of such information and data. In order to ensure your interest, we suggest you chose the products posted by our gold suppliers or VIP members.