Sandy Agent CM618

1. Brief Introduction

CM600 is an excellent polar fatty acid ester electrostatic agent for powder coatings.

2. Specification

3. Properties

①. CM600 prevents building up of direct current potentials during electrostatic powder spray coating. This allows, particularly with high direct current voltages, for the output speed, be increased and uniform thick film coatings, especially at object edges and ends, can be achieved.

②. AS a high melting point, it provides improved storage stability of the powder coating.

4. Application Fields

Electrostatic agent for powder coatings.

5. Recommended Dosage

①. Based on total formula: Approx 0.2-0.8%.

②. CM600 is added to the binder/pigment blend before extrusion.

Sandy Agent CM618

1. Brief Introduction

CM618 is one of PE Wax, improving of PEFE, it has very fine particle size. When use in the powder coating, it can’s together with resin, it can cause the film very even sandy texture, improving other properties, is one of perfect artistic additive.

2. Specification

3. Application

① It suitable for all type of powder coatings, use to make sandy texture in the film.

② The dosage of CM618 is: 0.3-1.5%, among whole formulation. Actual dosage shall be tested in lab.

③ Usage: it can be added directly or mixed with other material and then extruded out.

④ The sandy texture is base on the mount of CM618, particle size, and the thickness of film. The less amount of CM618, the smaller of sandy texture the big of particle size, the gibber of sandy texture. The thick of film, the bigger of sandy texture.

⑤ When use of CM618 don’t need to use flow agent, actual base on the test in lad.

⑥ When use of CM618, the powder coating have very good feature of smooth and anti-agglomeration.

⑦ When use of CM618, the film have very good feature of smooth and anti-abrasion.

⑧ It doesn’t contain silicon and ketone.

4. Package and Storage

Packing with PE bag,Net weight 10 kg per bag.

Keep in the cool and dry place, far away from fire. This material don’t contain toxic material, but wear dust-mask before operation.