4140 Cold Drawn Alloy Steel Round Bar-Cold Finished

  • Post Date:

    Jun 07,2013
  • Expiry Date:

    Jun 07,2014
  • Detailed Description:

    Cas No. :Unite Steel Quantity: 5Metric Tons
    Price:800 USD Metric Tons
    Payment Method: T/T or L/C
    Applications
    4140 Cold Drawn Alloy Steel Round Bar is the most commonly used of the high tensile steels with a wide range of applications in automotive, Gear and Engine construction, Crankshafts, Steering, knuckles, Connecting rods, Spindles, Intermediate gears, Pump and Gear shafts, Axles, Nuts and Bolts, Machined components, pump shafts, valves, fasteners, machine tools, dairy equipments, surgical & medical parts, threaded bars, studs, bolts, pins, hinges and handles.


    Back to Top
    Quality Standard
    ASTM A108 Standard Specification for Steel Bar, Carbon and Alloy, Cold-Finished
    EN 10277 Bright steel products.
    EN 10278 Dimensions and tolerances of bright steel products
    GB/T 905 Dimension, shape, weight and tolerance for cold-drawn round, square and hexagonal steels
    GB/T 3078 Technical Requirements for Quality Structural Steels Cold Drawn Bar


    Back to Top
    All Grades Comparison

    Material no. BS970 ASTM A29 JIS G4105 AS 1444 EN10083
    1.7225 En19A/708M40 4140
    Back to Top
    Chemical Composition(%)
    C Mn Si P S Cr Mo
    0.38-0.43 0.75-1.00 0.15-0.35 0.030 max 0.040 max 0.80-1.10 0.15-0.25
    Back to Top
    Mechanical Properties( T=20°C if not differently stated )
    Dia(mm) Tensile Strength Rm (Mpa) Yield Strength R2 (Mpa) Fracture elongation A5 (%) Hardness (HB)
    18-40 1000-1200 750 min 11 min 295-360
    40-80 900-1100 650 min 12 min 265-330
    Back to Top
    Diameter Tolerance
    Diameter Tolerance H9 Tolerance H10 Tolerance H11 Tolerance H12
    (mm) (mm) (mm) (mm) (mm)
    3 (+0,-0.025) (+0,-0.040) (+0,-0.060) (+0,-0.150)
    3-6 (+0,-0.030) (+0,-0.048) (+0,-0.075) (+0,-0.120)
    6-10 (+0,-0.036) (+0,-0.058) (+0,-0.090) (+0,-0.150)
    10-18 (+0,-0.043) (+0,-0.070) (+0,-0.110) (+0,-0.180)
    18-30 (+0,-0.052) (+0,-0.084) (+0,-0.130) (+0,-0.210)
    30-50 (+0,-0.062) (+0,-0.100) (+0,-0.160) (+0,-0.250)
    50-80 (+0,-0.074) (+0,-0.120) (+0,-0.190) (+0,-0.300)
    Back to Top
    Straightness Tolerance
    Diameter(mm) Straightness(mm/mtr)(max) Total Straightness(mm)(max)
    7-25 3 Total length*Max Straightness
    25-50 2 Total length*Max Straightness
    50-80 1 Total length*Max Straightness
    Back to Top
    Length Tolerance
    Cut to Lengthup to 9000Corresponding to specifications

    Type of Length Length(mm) Length Tolerance(mm)
    Manufacturing Length 3000-9000 +/-500
    Stock Length 3000 or 6000 (-0,+200)
    Back to Top
    Process
    Step1: Our process begins with either hot-rolled steel coils or hot-rolled straight bars from the mill. When hot-rolled bars are used, they are drawn individually. When coils are used, overhead cranes use C-hooks to safely lift the coil onto the “Payoff-Decoiler.”
    Step2: Steel unwraps from the “Payoff De-Coiler” and is fed through the horizontal and vertical pre-straightener rollers to “break the memory” of the coil.
    Step3: Steel continues on through the shot blaster so that the surface of the bar can be cleaned of all scale and rust.
    Step4: Now the steel is push-pointed through a die. The drawing unit will then pull the steel through that same die, in a continuous motion.
    Step5: Continuous straightening is maintained by passing the steel through more rollers.
    Step6: Non-destructive testing is in place on all drive lines to ensure that surface defects from the raw materials are being detected and sorted out.
    Step7: More straightening processes are in place throughout the draw line.
    Step8: Shear barrels or shear knives will shear or cut the bar to the customer’s desired length.
    Step9: The final straightening process occurs at the 2-roll straightener when the bar passes through the large concave and convex rolls. Guide blades, angles and pressure all contribute to the final straightness of the bar.

    Back to Top
    Weldability
    Parts should be welded in the hardened and tempered condition. Strength properties of the joint will not be the same as the base metal. Preheat 300-400ºC. Temper after welding to about 35-50ºC below the recommended tempering temperature.Filler metal: – FOX CM2-KB electrodes or CM2-IGwire. For advice in connection with difficult welding, please consult our engineers.


    Back to Top
    Packaging
    Lengths of 48″ and under are bundled and strapped to skids, or put in corrugated shipping containers. Longer lengths are shipped in 1,000lb bundles, 5 bands per bundle.




    Shanghai Unite Steel CO.,LTD

    Cindy Liu
    Tel: +86--021--35316960-811
    Fax: +86--021--35316961
    Email:cindyliu@shunitesteel.com
    www.shunitesteel.com
    www.shunitesteel.com.cn
  • CAS Registry Number:

    Unite Steel
  • Company:

    Shanghai Unite Steel Trading Co., Ltd.     [ China ]        
  • Contact:

    Cindy Liu
  • Tel:

    86-21-35316960-811
  • Fax:

    86-21-35316961
  • Email:

    cindyliu@shunitesteel.com
Inquiry
Home Suppliers Product CAS Gmall