Cast-iron Enamel Frits

• Post Date:

  Nov 04,2024

• Expiry Date:

  Nov 04,2025

• Detailed Description:

  Cast-iron Enamel Frits
  Reference No. Description
  Expansion Firing Application
  Coefficient (107) Temperature (°
  C)
  UNI-125 cast iron black enamel
  334.2 760-780
  UNI-126 cast iron black enamel
  332.4 760-780
  UNI-622 thick cast iron black
  enamel 314.4 750-780
  UNI-623 thick cast-iron black
  enamel 271.4 780-800
  UNI-625 cast-iron black enamel
  244 760-780
  UNI-308 cast-iron transparent
  enamel 332.1 760-780
  UNI-1271 thick cast iron black
  enamel 274 750-780
  UNI-1308 cast-iron transparent
  enamel 283.1 760-780
  UNI-1309 cast-iron transparent
  enamel 335.5 740-760
  UNI-2700 cast-iron opaque enamel
  289 780-800
  UNI-2707 acid resistant cast iron
  black enamel 305.6 780-800
  UNI-2708 cast-iron white cover
  coat 302.4 800-820
  UNI-2709 acid resistant cast-iron
  white cover coat 310.2 820-850
  Note: enameling on surface of
  cast iron, as called Wet-way
  Coating enamel first, cleaning
  the surface of earthen bowl after
  anneal .
  
  1 Milling additon ratio for cast-
  iron black enamel:
  frit 100 clay 5-7
  quartz powder 0-5 borax 0.5-0.8
  sodium nitrite 0.2 black
  pigment 2-5
  water 50-55 ml
  note: adding 10-20% quartz powder
  in acid resistant black enamel
  frit slurry fineness 0.5-
  1.0g/150mesh.100 ml specific
  gravity 160-170g/100ml
  2 cast iron opaque enamel(sub-
  opaque enamel )
  frit 100 clay 5-6
  borax 0.5-0.8 aluminium oxide 2
  water 45-50ml
  note: sub-opaque enamel consist
  of cast iron opaque enamel,with
  same milling addition ratio.
  frit slurry fineness 1-
  1.5g/150¡¤100ml specific
  gravity 160-165g/100ml
  