High purity Fire Retardant Magnesium Hydroxide

• Post Date:

  Jun 24,2017

• Expiry Date:

  Jun 24,2018

• Detailed Description:

  Quantity: 25Kilograms
  Specs:purity: 99.8%, particle size:D50 is 0.7-1.1um
  Payment Method: T/T. L/C, West Union
  Major features:
  1. High purity, content of magnesium hydroxide Mg(OH)2 is exceeded 99%, actual content is 99.8%
  2. Good dispersion, with speical surface treatment, improve the compatibility with plastic.
  3. Narrow distribution of particle size and D50 is 0.7-1.1 um, which can be added to plastic more easily.
  4. Hexagonal platelet of particle is better combine with plastic.
  5. We were honored with advanced and representative company by Chinese government at 2015
  6. With ISO9000, SGS, REACH etc certificates
  
  YR6 Serial Magnesium hydroxide Features and Main application:
  
  YR6 Serail Magnesium hydroxide fire-retardant is high purity Mg(OH)2,the surface is specially treated with vinyl silane, stearic acid, compound vinyl silane, compound,amino silane, Polymer
  because surface is after organic reaction,so it greatly reduces surface energy, and improves the dispersion and liquidity in organic matter accordingly,
  as a no halogen flame retardant,it can be used in plastic. such as PE,PP EPDM ,Rubber.Low smoke density and high thermal stability. initial decomposition temperature is about 340 degrees centigrade.No Poisonous and causticity air when degradation.
  Because of vinylsilane surface treatment,it is good for improving the compatibility of polymer and filler when casting mold and modification.
  With pretreatment of powder when chemical reaction,it will deduce clients’ input for facility and processing steps.further Lower the cost of facility and labor
  
  Technical parameters:
  
  Physical status white powder
  Mg(OH)2 99.6%
  CaO Max 0.03%
  Cl Max 0.01%
  Fe Max 0.01%
  Whiteness Min 96
  drying shrinkage(110 degree centigrade,1h) max0.06%
  D50(particle size) 0.7-1.1μm
  particle shape hexagonal platelet
  insoluble matter in hydrochloric acid max0.01%
  loss on ignition(1200 degree centigrade) Min 30.5%
  specific surface area 6-8 m2/g
  mohs hardness 2.5
  bulk density 300-500 kg/m3
  Initial dehydration temperature 340 degree centigrade
  electrical conductivity 391 uS/cm
  
  Main application and advantage:
  As a non-halogen flame retardant, It can be adopted in plastics and elastomers. low smoke density and high thermal stability, initial decomposition temperature  is about 340 degrees centigrade . Suitable for high-temperature mixing processing, good dispersion and fluidity in the resin, and also can improve the compatibility of polyester.
  As a high loading and additive flame retardant, It can be widely used as fire retardant and smoke suppressant in range of plastics and rubber, such as PE, PP, PVC, EVA, ABS, TPE etc.
  it can replace organic flame retardants, inorganic flame retardant ATH, which can greatly improve the thermal stability. Reduce the abrasion of machine and mold made by inorganic flame retardant. Prolong working life of facility,     
  Magnesium hydroxide after surface treatment can be filled to organic material in high density, improving the materials performance.
  
  
  Contact
  Ada Sun
  Shandong Yinrui Flame Retardant Material Co.,Ltd.
  Whatsapp/Mobile:+8615953178602
  QQ:1416905614
  We're sure we will supply the best service and price for you

• Company:

  Shandong Yinrui Flame Retardant Material Co., Ltd     [ China ]        

• Contact:

  Ada Sun

• Tel:

  86053181171917

• Fax:

  86053184210911

• Email:

  ada1993@sdyinrui.com