    This master batch of Antimony Trioxide (Sb2O3)is designed to eliminate the pollution brought by powder. It can be compounded with polymers without modified particle-shaping and features in fine disperse properties. The anti-impact strength of polymers with this master batch is remarkably improved as compared to these of the powder Antimony Trioxide (Sb2O3), which make it applicable in such polymer as PA6, PA66, ABS, PP, PE, PBT, PVC, HIPS,, etc..
     
    Technical Indexes:
    Item
    Index
    Appearance
    White Pellets
    Particle Size
    Φ3mm×2mm
     Sb2O3
    90 %
    Whiteness
    ≥95
    Moisture
    ≤0.2%
    PbO
    ≤0.06%
    As
    ≤0.04%
    Cu
    ≤0.0013%
    Se
    ≤0.0008%
    Fe
    ≤0.0014%
    Cd
    ≤0.0008%
     
    Applications:
    FR-M1220 could be directly blent with resin and appropriate amount of master batch of decabromodiphenyl oxide (or other halogen flame retarding agent). The particle-shaping can be achieved by injection or twin-screw extrusion after mixed.
     
     Packing:25Kg or 1000Kg plastic woven bag
     
    Recommended:
    Resin
    ABS
    HIPS
    PA
    Master Batch
    FR-M1210(%)
    FR-M1220(%)
    FR-M1210(%)
    FR-M1220(%)
    FR-M1210(%)
    FR-M1220(%)
    V-0
    12
    5
    12
    5
    13.5
    5.5
    V-1
    11.0
    4.2
    11.0
    4.2
    11.5
    4.5
    V-2
    10
    3.5
    10
    3.5
    10.5
    3.5
    HB
    2.5
    1
    2.5
    0.8
    4.5
    1.5
     
    Application:(ABS)
    Property
    Unit
    Method
    1
    2
    Simple Beam Notch Impact Strength
    KJ/m2
    GB/T 1043
    8.0
    8.9
    Izod Impact Strength
    KJ/m2
    GB/T 1843
    8.2
    7.4
    Average Shrinkage
    %
    HG-112
    -0.70
    -0.57
    Tensile Strength
    MPa
    GB/T 1040
    42.5
    42
    Elongation at Break
    %
    GB/T 1040
    20
    25
    Simple Beam Impact Strength
    KJ/m2
    GB/T 1043
    58.5
    63.5
    UL 94
    -
    ANSI/UL 94
    V-0
    V-0
    LOI
    %
    ASTM-2863
    26.5
    29.8
    Maximum Smoke Density
    -
    ASTM E-662
    266.6
    247.5
    Thermal Distortion Temperature
    ℃
    GB 1634
    95.5
    97
     
    Formulation 1: ABS 82%;Saytex102E(powder) 12.5%;Sb2O3 (powder) 4.5%; other additive 1%
    Formulation 2:  ABS 80%;FR-M1220 4.5% ; FR-M1210 14.5%;other additive 1%
     
    Dose recommended:
    Resin
    ABS
    HIPS
    PA
    Master Batch
    FR-M8010 (%)
    FR-M1220(%)
    FR-M8010 (%)
    FR-M1220(%)
    FR-M8010 (%)
    FR-M1220(%)
    V-0
    11.5
    5
    11.5
    5
    13.5
    5
    V-1
    11.0
    4.5
    11.0
    4.5
    11.5
    4.5
    V-2
    10.5
    3.5
    10.5
    3.5
    11
    3.5
    HB
    2.5
    1
    2.5
    0.8
    5
    1.5
     
    Application Information:(ABS)
     
    Property
    Unit
    Method
    1
    2
    Simple Beam Notch Impact Strength
    KJ/m2
    GB/T 1043
    8
    11.5
    Izod Impact Strength
    KJ/m2
    GB/T 1843
    8.2
    9.5
    Average Shrinkage
    %
    HG-112
    -0.72
    -0.6
    Tensile Strength
    MPa
    GB/T 1040
    42.5
    42.2
    Elongation at Break
    %
    GB/T 1040
    21
    26.5
    Simple Beam Impact Strength
    KJ/m2
    GB/T 1043
    58.5
    62.5
    UL 94
    -
    ANSI/UL 94
    V-0
    V-0
    LOI
    %
    ASTM-2863
    26.5
    28
    Maximum Smoke Density
    -
    ASTM E-662
    265
    170
    Thermal Distortion Temperature
    ℃
    GB 1634
    95
    95
     
    Formulation 1:ABS 82.3%;Saytex8010(powder) 12.5%;Sb2O3 (powder) 4.2%; other additive 1%
    Formulation 2:  ABS 80%;FR-M1220 4.5% ;  FR-M8010  14.5%; other additive 1
     
    Dose recommended:
     
    ABS %
    HIPS %
    PA %
    V-0
    17
    17
    18
    V-1
    14
    14
    14
    V-2
    12.5
    12.5
    12.5
    HB
    3.5
    3.5
    6.5
     
    Application Information:(ABS 757K)
    Property
    Unit
    Method
    1
    2
    Tensile Strength
    MPa
    GB/T 1040
    42.5
    41.5
    Elongation at Break
    %
    GB/T 1040
    20
    25
    Simple Beam Impact Strength
    KJ/m2
    GB/T 1043
    58.5
    63.5
    Simple Beam Notch Impact Strength
    KJ/m2
    GB/T 1043
    8
    8.5
    Izod Notch Impact Strength
    KJ/m2
    GB/T 1843
    8.3
    8.9
    Average Dimension Change
    %
    HG-112
    -0.71
    -0.65
    UL 94
    -
    ANSI/UL 94
    V-0
    V-0
    LOI
    %
    ASTM-2863
    26.5
    29.5
    Maximum Smoke Density
    -
    ASTM E-662
    268.5
    244.5
    Thermal Distortion Temperature
    ℃
    GB 1634
    96
    96
    Formulation 1:ABS 83%;DBDPO 12%;Sb2O3 4%;other 1%
    Formulation 2:ABS 83%;FR2000 17%
     
    Dose recommended:
     
    ABS %
    HIPS %
    PA %
    V-0
    16.7
    16.7
    18.2
    V-1
    14.2
    14.2
    14.2
    V-2
    12.5
    12.5
    12.5
    HB
    3.2
    3.2
    6.3
     
    Application Information:(ABS 757K)
    Property
    Unit
    Method
    1
    2
    Tensile Strength
    MPa
    GB/T 1040
    42.5
    41.5
    Elongation at Break
    %
    GB/T 1040
    20
    25
    Simple Beam Impact Strength
    KJ/m2
    GB/T 1043
    58.5
    63.5
    Simple Beam Notch Impact Strength
    KJ/m2
    GB/T 1043
    8
    8.5
    Izod Notch Impact Strength
    KJ/m2
    GB/T 1843
    8.2
    9
    Average Dimension Change
    %
    HG-112
    -0.70
    -0.65
    UL 94
    -
    ANSI/UL 94
    V-0
    V-0
    LOI
    %
    ASTM-2863
    26.5
    28
    Maximum Smoke Density
    -
    ASTM E-662
    265.5
    169.5
    Thermal Distortion Temperature
    ℃
    GB 1634
    96
    94
     
    Formulation 1:ABS 83%;DBDPE 125%;Sb2O3 4% ;other 1%
    Formulation 2:ABS 83%;FR3000 17%

  • Company:

    Weifang Yucheng Chemical Co.,Ltd.     [ China ]        

  • Contact:

    MR.ALLAN WEI(MANAGER) 013906369909

  • Tel:

    +86-536-8291528 8291538 013906

  • Fax:

    +86-536-8291558

  • Email:

    brom@163169.net
Inquiry
Home Suppliers Product CAS Gmall