Product Description |
|
Low Cure Powder Coatings are specially formulated and manufactured to provide substrate protection and durability for a wide range of applications with the advantage of enhanced process-ability over standard cure powders. |
|
Popular Applications |
|
Appliances AC compressors Electric motors Automotive radiators Heavy mass castings such as sewing machine stands, auto springs |
|
General Specifications |
|
Specific Gravity: 1.6 ± 0.3 depending on product Particle Size Distribution: < 125 microns 100% passing Curing Schedule: 150°C (object temperature) for 10 minutes Shelf Life: 6 months minimum when stored at temperature |
|
< 25°C and RH < 60% |
General Film Properties
|
Property |
Test Method |
Value |
|
Recommended Film Thickness |
ASTM D-1186 |
50–60 microns minimum |
|
Gloss Range @ 60° Gloss Head |
Changming Standard |
55–95% |
|
Impact Resistance |
ASTM D-2794 |
80 kg-cm* |
|
Erichsen Cupping |
ASTM E-643 |
6 mm, min |
|
Flexibility |
ASTM D-552 |
6mm, min |
|
Scratch Hardness |
BS 3900 Part E6 |
2 kgs min |
|
Salt spray Resistance |
ASTM B-117 |
500–1000 hrs depending on finish |
|
Humidity Resistance |
ASTM B-2247 |
500–1000 hrs depending on finish |
|
QUV Resistance |
ASTM G-53 |
Not applicable |
|
Pencil Hardness |
ASTM D-3363 |
H–2H |