iron oxide red anticorrosion protective primer

SWD959 Series SH130 One component

  moisture cure polyurethane (rigid) system

      iron oxide red anticorrosion protective primer

Descriptions                  Primer is the primary element of anticorrosion coating system. It should has high adhesive strength with substrate, high penetrate resistance with water, oxygen, ions, etc. The iron oxide red anticorrosion protective primer designed by SWD Urethane Co., USA has excellent properties except the performances above, for example, it also has good compatibility with polyurethane, epoxy, chlorinated rubber, alkyd and phenolic, etc. top coating which brings great convenience for the performance, it has been widely used in the Americas and Europe.

Characteristics             This primer product through special precision formulation and scientific process takes one component polyurea polyurethane resin and high quality iron oxide as main material. Coating is dense, tough, with high plugging performance and penetrates resistance, excellent performances of rust resistance, anticorrosion, water and wet resistance, high adhesive strength with metal substrate, bond well with the following coatings. One component product is easy to use, can be working in simple surface treatment substrates.

Specifications

Adhesive strength                            11.5Mpa

Impact resistance                             ≥50kg•cm

Temperature variation                         -40------+180℃

Wear resistance（700g/500r）                  15mg

Acid resistance 30%H₂SO₄ or 15%HCI, 30d        no rust no bubbles no peel

Alkali resistance 30%NaOH, 30d                 no rust no bubbles no peel

Salt resistance 80g/L, 30d                       no rust no bubbles no peel

Salt spray resistance 1000h                      no rust no bubbles no peel

Oil resistance 0# diesel Crude oil 30d              no rust no bubbles no peel

Data of performance

Color                        Multiple colors as customers’ need

Luster                        half glazed

Density                       1.25g/cm³

Volume solid content            77%±2%

VOC                         ≤186g/L

Recommended dry film thickness   30-80μm

Theoretical coverage             0.08kg/sqm (calculated by the above solids percentage and dry film thickness of 50 microns)

Practical coverage                Allow appropriate loss rate

Dry time                       1-3h

Overcoating interval              min: 3h, max: 24h

Overcoating method              Airless spray, Air spray, Brush, Roller

Flash point                      57℃

Recommend procedures                        

Application scope           Industries and other fields anticorrosion coating.

Shelf life                  10 months (Indoor with dry and cool conditions)

Packing                    20kg/bucket. 25kg/bucket

Production area            Minhang District, City of Shanghai (10% of raw materials imported from SWD US)

Security                   To apply this product must be accordance with the relevant national regulation of sanitation, safety and environment. Avoid contacting the wet coating.

Global applicability         Our company aims to provide worldwide customers the same coatings, but sometimes, some small adjustments are made to satisfy each region conditions and international norms, in this case, an alternative product data will be provided.

Integrity declaration         Our company guarantees the reality of the listed data, due to the diversity and variability of the application environment, please test and verify it before use. We don’t take any other responsibilities except the coating quality self and reserve the right of modification the listed data without prior notice.